摘要：木材本身是一种可再生的环保性能较好的材料，但是天然的木材具有较高的含水率，并且随着外界的温度和湿度的变化，木材容易产生干缩或湿胀现象。这对木材在工业中的利用非常不利，木材的干缩湿胀会导致木材发生开裂，变形，翘曲以及腐朽等。这些危害都会大大降低木材在实际生产应用中的利用率。因此需要对木材进行改性以提高木材的尺寸稳定性。这也使得每年都会有大量的关于木材改性方面的论文发表。关于本课题的研究大都集中在丙烯酸酯乳液和石蜡乳液的制备和性能测定方面，以及这些复合乳液对材料尺寸稳定性的影响。
关键词：丙烯酸酯 石蜡 乳化剂 性能测定 木材改性
Research and Review on Effect of acrylate / paraffin emulsion on dimensional stability of wood
Abstract: Wood itself is a kind of renewable material with good environmental protection performance, but natural wood has high moisture content, and with the change of temperature and humidity outside, wood tends to shrink or swell. This is very disadvantageous to the use of wood in industry. Wood shrinkage and swelling will lead to wood cracking, deformation, warping and decay. These hazards will greatly reduce the utilization rate of wood in practical production and application. Therefore, wood modification is needed to improve the dimensional stability of wood. This also makes a large number of papers on wood modification published every year. Most of the research focused on the preparation and performance evaluation of acrylate emulsion and paraffin emulsion, and the effect of these composite emulsions on dimensional stability of materials.
Keyword: acrylate； paraffin wax； emulsifier； Performance measurement； Wood modification
一、研究现状
（一）乳液聚合技术
乳液聚合工艺一般可分为两种：核壳乳液聚合和无皂乳液聚合。核壳乳液聚合是把两种或者多种不同性质的物质在一定条件下聚合，由于聚合的成分不同从而使得聚合物乳液的性能有了很大的提高。核壳乳液聚合中由于核壳层之间存在接枝、互穿聚合物网络以及离子键合，所以表现出较好的成膜性、稳定性以及防水性。无皂乳液聚合一般用来制备尺寸均一、具有多功能基团的聚合物乳液。这种方法可以消除传统乳液聚合技术由于乳化剂的吸附对乳液造成的稳定性、成膜性、耐水性等的影响。这两种聚合技术都复合经济效益并且对环境友好，因此普遍受到社会各界的重视，大都采用这两种技术来制备相关的复合乳液。