文献综述
硅烷改性纤维素纤维增强聚丙烯的制备及取代度影响探究
摘要：纤维素,自然界的一种天然高分子材料，它绿色环保且数量十分可观，在很多行业纤维素都占据了令人瞩目的高度。天然纤维素纤维表面存在大量的羟基，导致分子之间极易形成氢键，外部表现为极易团聚，这是我们需要克服的问题。
本研究主要方向是利用硅烷改性纤维素纤维，再使用改性纤维增强聚丙烯力学性能。实验中，利用化学气相沉积法，以三甲氧基硅烷反应取代纤维素纤维链表面面的羟基，对纤维素进行疏水改性，以达到提高纤维素和聚丙烯之间的相容性，并制备纤维素增强聚丙烯复合材料。
Abstract：Cellulose, a natural polymer material in nature, is environmentally friendly and has a considerable amount of cellulose. In many industries, cellulose has occupied an impressive height. There are a large number of hydroxyl groups on the surface of natural cellulose fibers, which leads to the formation of hydrogen bonds easily between molecules, and the external appearance is extremely easy to agglomerate. This is a problem we need to overcome.
The main direction of this research is to use silane-modified cellulose fiber. In the experiment, chemical vapor deposition method is used to replace the hydroxyl group on the surface of the cellulose fiber chain with trimethoxysilane reaction, and the cellulose is hydrophobically modified to improve the fiber. Compatibility between the prime and polypropylene, and preparation of a cellulose reinforced polypropylene composite.
关键词：纤维素；硅烷改性；聚丙烯；三甲氧基硅烷
1纤维素
纤维素化学分子式为(C6H10O5)n。是这一时间段地球上天然有机材料里面储量极其巨大，来源极其广泛的绿色环保材料。[1]以其良好的力学性能，较高的拉伸模量，杨氏模量，以及较低的热膨胀系数，因此成为了一种十分不错的增强材料(分子结构如图1)。纤维素有较强的机械性能。纤维素由于具有十分出色的性能而在橡胶工业、涂料工业等行业当中有着令人期待的前景[2-3]。纤维素作为增强材料，成本低且可以循环使用，符合绿色环保的要求。作为高等植被成熟细胞中大量存在的物质，木材里的纤维素大约占到了40%-50%，在禾本科植被如竹子、甘蔗、玉米的茎干中的含量大致在40%-45%之间，尤其在棉花中的含量达到了最高，甚至达到了99%。天然纤维素由于其结构的特点，纤维素分子中含有大量羟基，造成了纤维素之间极易形成氢键，使得纤维素之间极易团聚从而影响增强效果。