铁钡氧体对水泥净浆超声波波速影响研究
摘要
超声波在混凝土无损检测中的应用日益广泛。本文结合对水泥净浆试件的超声波检测实验，探究讨了铁钡氧体对超声波在水泥净浆中传播波速的影响，以助于更全面更深入的在水泥材料无损检测中利用超声波，并结合国内外研究现状对本课题的可行性进行分析。本文主要探究不同掺量（0%、5%、10%、15%、20%）的铁钡氧体对水泥净浆超声波波速的影响规律微观结构（孔隙率、孔径分布、微观形貌）和力学性能（抗折强度、抗压强度）的影响。研究不同龄期（1d、3d、7d、14d、28d、56d、91d）净浆试件的超声波波速，探究铁钡氧体对水泥净浆超声波波速影响的规律。此外，本文还研究了不同掺量的铁钡氧体对水泥净浆力学性能和微观结构的影响。
关键词：铁钡氧体；水泥净浆；超声波波速；力学性能
Abstract
Ultrasonic is widely used in nondestructive testing of concrete. In this paper, the effect of BaFe12O19 on the wave velocity cement paste is discussed, which is helpful to use ultrasonic technique in non-destructive testing of cement-based materials more comprehensively and deeply. In this paper, the influence of BaFe12O19 with different contents (0%, 5%, 10%, 15%, 20%) on ultrasonic wave velocity of cement paste was investigated. In addition, the effects of different contents of BaFe12O19 on the mechanical properties and microstructure of cement paste were studied.
Keywords: BaFe12O19；Cement paste; Ultrasonic Wave Velocity; Mechanical Properties
引言
水泥作为一种历史悠久的建筑材料，被广泛应用于我们的现实生活中。新时代的建材随着科技和经济的持续发展，人们对新型科技的研究也逐步地深入钡铁氧体材料具有较大的矫顽力和单轴磁晶各向异性等优点，同时还拥有高电阻率、良好的化学稳定性和低成本等优点，被广泛应用于微波吸收领域。将水泥材料与钡铁氧体的结合能够发挥出不错的效果。我国经济的飞速发展以及城镇化进程的加快，建筑行业得到了突飞猛进的发展。混凝土质量直接决定了建筑的质量，进而影响人们的生命安全。因此,混凝土强度的检测方法受到了社会各界的广泛关注。在传统的检验过程中,取样试件的代表性一直是个问题。西方研究人员在混凝土结构检测中首次使用超声脉冲检测技术以来,这种无损检测技术得到了广泛应用。超声波技术能够对混凝土的强度、弹性、内部缺陷等进行检测，但是，由于强度检测中的多种不确定性因素，导致了超声测强技术发展缓慢。但是，随着科技研究与理论研究的深入发展，超声测强的应用深度与广度会进一 步增大。由于新型材料的产生我们使用超声波对其检测时因为钡铁氧体的吸波特性会给检测结果带来不可知的影响。为此探究钡铁氧体对超声波在水泥材料中影响能够更好了解新型材料的特性，并且将安全隐患及时排除，为建筑的检测与保养提供便利性。
以上是毕业论文文献综述，课题毕业论文、任务书、外文翻译、程序设计、图纸设计等资料可联系客服协助查找。